We welded a 4 inches tube 3/16'' wall. The base metal
is SS 304L and the filler is 308L. The tube corroded
in a Chloride environment at the HAZ. We understand
why it corroded but we do not see the reason why it is
intergranular. Carbon has been verified for base and
filler metal and is approx 0.02%. Someone has an idea?
Carbide precipitation and chromium depletion should
not be a factor whith the L grade?